Multilayered ceramic capacitor and board for mounting the same

ABSTRACT

There is provided a multilayered ceramic capacitor including: a ceramic body in which a plurality of dielectric layers are stacked; an active layer including a plurality of first and second internal electrodes formed to be alternately exposed to both end surfaces of the ceramic body, having the dielectric layer interposed therebetween, to form capacitance; an upper cover layer formed above the active layer, a lower cover layer formed below the active layer and being thicker than the upper cover layer; and first and second external electrodes formed to cover both end surfaces of the ceramic body, wherein a ratio of an area Y of a region overlapped between the first and second internal electrodes to a total area X of the active layer and the upper cover layer on a cross section of the ceramic body in length-thickness (L-T) directions is in a range of 0.5 to 0.9.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the priority of Korean Patent Application No.10-2012-0138920 filed on Dec. 3, 2012, in the Korean IntellectualProperty Office, the disclosure of which is incorporated herein byreference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a multilayered ceramic capacitor and aboard for mounting the same.

2. Description of the Related Art

In general, multilayered ceramic capacitors, multilayered chipelectronic components, are chip shaped condensers mounted on printedcircuit boards of various electronic products such as display devices,for example, liquid crystal displays (LCDs), plasma display panels(PDPs), and the like, computers, smart phones, mobile phones, and thelike, serving to charge or discharge electricity.

Since this multilayered ceramic capacitor (MLCC) has advantages such asa small size, high capacitance, ease of mounting, or the like, themultilayered ceramic capacitor may be used as a component of variouselectronic devices.

The multilayered ceramic capacitor may have a structure in which aplurality of dielectric layers and internal electrodes having oppositepolarities while having the dielectric layer interposed therebetween arealternately stacked.

Since the dielectric layers have piezoelectric and electrostrictiveproperties, when direct current (DC) or alternating current (AC) voltageis applied to the multilayered ceramic capacitor, a piezoelectricphenomenon is generated between the internal electrodes, thereby causingvibrations.

These vibrations may be transferred to a printed circuit board on whichthe multilayered ceramic capacitor is mounted through a solder of themultilayered ceramic capacitor, such that the entire printed circuitboard may become an acoustic reflective surface generating a vibrationsound, known as noise.

The vibration sound may have a frequency corresponding to an audiofrequency in a region of 20 to 20000 Hz, making a person uncomfortable.The vibration sound making the person uncomfortable as described aboveis known as acoustic noise.

In order to reduce acoustic noise, research into a product having a formin which a thickness of a lower cover layer of the multilayered ceramiccapacitor is increased has been conducted.

In addition, when the multilayered ceramic capacitor having theincreased thickness of the lower cover layer is mounted on the printedcircuit board, the thick lower cover layer may be positioned in alowermost position so as to be advantageous in decreasing acousticnoise, such that the multilayered ceramic capacitor may be mounted in ahorizontal mounting scheme.

Meanwhile, in the case of a product having a form in which the thicknessof the lower cover layer of the multilayered ceramic capacitor isincreased in order to reduce acoustic noise, a crack defect or adelamination defect may be generated in a sintering process due to adifference in density between a region in which the internal electrodesare formed and a region in which the internal electrodes are not formed.

RELATED ART DOCUMENT

-   (Patent Document 1) Japanese Patent Laid-Open Publication No.    2006-203165

SUMMARY OF THE INVENTION

An aspect of the present invention provides a multilayered ceramiccapacitor and a board for mounting the same.

According to an aspect of the present invention, there is provided amultilayered ceramic capacitor including: a ceramic body in which aplurality of dielectric layers are stacked; an active layer including aplurality of first and second internal electrodes formed to bealternately exposed to both end surfaces of the ceramic body, having thedielectric layer interposed therebetween, to form capacitance; an uppercover layer formed above the active layer, a lower cover layer formedbelow the active layer and being thicker than the upper cover layer; andfirst and second external electrodes formed to cover both end surfacesof the ceramic body, wherein a ratio of an area Y of a region overlappedbetween the first and second internal electrodes to a total area X ofthe active layer and the upper cover layer on a cross section of theceramic body in length-thickness (L-T) directions is in a range of 0.5to 0.9.

When half of a total thickness of the ceramic body is defined as A, athickness of the lower cover layer is defined as B, half of a totalthickness of the active layer is defined as C, and a thickness of theupper cover layer is defined as D, a ratio ((B+C)/A) of deviationbetween a center of the active layer and a center of the ceramic bodymay be in a range of 1.063 to 1.745 (1.063≦(B+C)/A≦1.745).

When a thickness of the lower cover layer is defined as B and athickness of the upper cover layer is defined as D, a ratio (D/B) of thethickness D of the upper cover layer to the thickness B of the lowercover layer may be in a range of 0.021 to 0.422 (0.021≦D/B≦0.422).

When half of a total thickness of the ceramic body is defined as A and athickness of the lower cover layer is defined as B, a ratio (B/A) of thethickness B of the lower cover layer to the half A of the totalthickness of the ceramic body may be in a range of 0.329 to 1.522(0.329≦B/A≦1.522).

When a thickness of the lower cover layer is defined as B and half of atotal thickness of the active layer is defined as C, a ratio (C/B) ofthe half C of the total thickness of the active layer to the thickness Bof the lower cover layer may be in a range of 0.146 to 2.458(0.146≦C/B≦2.458).

Points of inflection (PI) formed in the both end surfaces of the ceramicbody may be formed in positions lower than a center of the ceramic bodyin a thickness direction due to a difference between strain generated ina center of the active layer and strain generated in the lower coverlayer when voltage is applied thereto.

According to another aspect of the present invention, there is provideda board for mounting a multilayered ceramic capacitor, the boardincluding: a printed circuit board having first and second electrodepads formed thereon; and a multilayered ceramic capacitor mounted on theprinted circuit board, wherein the multilayered ceramic capacitorincludes a ceramic body in which a plurality of dielectric layers arestacked, an active layer including a plurality of first and secondinternal electrodes formed to be alternately exposed to both endsurfaces of the ceramic body, having the dielectric layer interposedtherebetween, to form capacitance, an upper cover layer formed above theactive layer, a lower cover layer formed below the active layer andbeing thicker than the upper cover layer; and first and second externalelectrodes formed on the both end surfaces of the ceramic body andconnected to the first and second electrode pads by soldering, and aratio of an area Y of a region overlapped between the first and secondinternal electrodes to a total area X of the active layer and the uppercover layer on a cross section of the ceramic body in length-thickness(L-T) directions may be in a range of 0.5 to 0.9.

When half of a total thickness of the ceramic body is defined as A, athickness of the lower cover layer is defined as B, half of a totalthickness of the active layer is defined as C, and a thickness of theupper cover layer is defined as D, a ratio ((B+C)/A) deviation between acenter of the active layer and a center of the ceramic body may be in arange of 1.063 to 1.745 (1.063≦(B+C)/A≦1.745).

When a thickness of the lower cover layer is defined as B and athickness of the upper cover layer is defined as D, a ratio (D/B) of thethickness D of the upper cover layer to the thickness B of the lowercover layer may be in a range of 0.021 to 0.422 (0.021≦D/B≦0.422).

When half of a total thickness of the ceramic body is defined as A and athickness of the lower cover layer is defined as B, a ratio (B/A) of thethickness B of the lower cover layer to the half A of the totalthickness of the ceramic body may be in a range of 0.329 to 1.522(0.329≦B/A≦1.522).

When a thickness of the lower cover layer is defined as B and half of atotal thickness of the active layer is defined as C, a ratio (C/B) ofthe half C of the total thickness of the active layer to the thickness Bof the lower cover layer may be in a range of 0.146 to 2.458(0.146≦C/B≦2.458).

Points of inflection (PI) formed in the both end surfaces of the ceramicbody may be formed in positions lower than a height of the soldering dueto a difference between strain generated in a center of the active layerand strain generated in the lower cover layer when voltage is appliedthereto.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other aspects, features and other advantages of thepresent invention will be more clearly understood from the followingdetailed description taken in conjunction with the accompanyingdrawings, in which:

FIG. 1 is a partially cut-away perspective view schematically showing amultilayered ceramic capacitor according to an embodiment of the presentinvention;

FIG. 2 is a cross-sectional view of the multilayered ceramic capacitorof FIG. 1 taken in a length direction;

FIG. 3 is a schematic cross-sectional view of the multilayered ceramiccapacitor of FIG. 1 taken in the length direction in order to describe adimensional relationship between components included in the multilayeredceramic capacitor;

FIG. 4 is a perspective view showing a form in which the multilayeredceramic capacitor of FIG. 1 is mounted on a printed circuit board;

FIG. 5 is a cross-sectional view of the multilayered ceramic capacitorand the printed circuit board of FIG. 4 taken in the length direction;and

FIG. 6 is a cross-sectional view schematically showing that themultilayered ceramic capacitor of FIG. 4 is deformed when voltage isapplied thereto in a state in which the multilayered ceramic capacitoris mounted on the printed circuit board.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Hereinafter, embodiments of the present invention will be described indetail with reference to the accompanying drawings.

The invention may, however, be embodied in many different forms andshould not be construed as being limited to the embodiments set forthherein. Rather, these embodiments are provided so that this disclosurewill be thorough and complete, and will fully convey the scope of theinvention to those skilled in the art.

In the drawings, the shapes and dimensions of components may beexaggerated for clarity, and the same reference numerals will be usedthroughout to designate the same or like components.

Directions of a hexahedron will be defined in order to clearly describethe embodiments of the present invention. L, W and T shown in theaccompanying drawings refer to a length direction, a width direction,and a thickness direction, respectively. Here, the thickness directionmay be used to have the same concept as that of a direction in whichdielectric layers are stacked.

Further, in the present embodiment, for convenience of explanation, adescription will be provided in a state in which surfaces of a ceramicbody on which first and second external electrodes are formed in thelength direction are set to both end surfaces and surfaces of theceramic body vertically intersecting with the both end surfaces are setto side surfaces.

In addition, an upper surface of the ceramic body on which an uppercover layer thereof is formed is represented by S_(T), and a lowersurface of the ceramic body on which a lower cover layer thereof isformed is represented by S_(B).

Hereinafter, embodiments of the present invention will now be describedin detail with reference to the accompanying drawings.

FIG. 1 is a partially cut-away perspective view schematically showing amultilayered ceramic capacitor according to an embodiment of the presentinvention.

FIG. 2 is a cross-sectional view of the multilayered ceramic capacitorof FIG. 1 taken in a length direction.

FIG. 3 is a schematic cross-sectional view of the multilayered ceramiccapacitor of FIG. 1 taken in the length direction in order to describe adimensional relationship between components included in the multilayeredceramic capacitor.

Referring to FIGS. 1 and 2, a multilayered ceramic capacitor 100according to the embodiment of the present invention may include aceramic body 110, an active layer 115 having first and second internalelectrodes 121 and 122, upper and lower cover layers 112 and 113, andfirst and second external electrodes 131 and 132 covering both endsurfaces of the ceramic body 110.

The ceramic body 110 may be formed by stacking a plurality of dielectriclayers 111 and sintering the same. In this case, a shape and a dimensionof the ceramic body 110 and the number of multilayered dielectric layers111 are not limited to those of the embodiment shown in the accompanyingdrawings.

In addition, the plurality of dielectric layers 111 configuring theceramic body 110 may be in a sintered state. Adjacent dielectric layers111 may be integrated such that a boundary therebetween may not beclearly discernible without using a scanning electron microscope (SEM).

The ceramic body 110 may include the active layer 115 as a partcontributing to forming capacitance of the capacitor and the upper andlower cover layers 112 and 113 formed as upper and lower margin parts onand beneath the active layer 115.

The active layer 115 may be formed by repeatedly stacking the first andsecond internal electrodes 131 and 132, having the dielectric layer 111interposed therebetween.

In this case, a thickness of the dielectric layer 111 may be optionallychanged according to capacitance design of the multilayered ceramiccapacitor 100, but an average thickness of a single dielectric layer maybe 0.1 μm to 10.0 μm after sintering. However, the present invention isnot limited thereto.

Further, the dielectric layer 111 may contain a ceramic powder havinghigh permittivity, for example, a barium titanate (BaTiO₃) based powderor a strontium titanate (SrTiO₃) based powder, or the like, but thepresent invention is not limited thereto.

The upper and lower cover layers 112 and 113 may have the same materialand configuration as those of the dielectric layer 111, except that theinternal electrodes are not included therein.

The upper and lower cover layers 112 and 113 may be formed by stacking asingle or two or more dielectric layers on upper and lower surfaces ofthe active layer 115 in a vertical direction, respectively. The upperand lower cover layers 112 and 113 may serve to prevent the first andsecond internal electrodes 121 and 122 from being damaged by physical orchemical stress.

In addition, the lower cover layer 113 may be thicker than the uppercover layer 112 by further increasing the number of stacked dielectriclayers as compared with the upper cover layer 112.

Meanwhile, the first and second internal electrodes 121 and 122, a pairof electrodes having different polarities from each other, may be formedby printing a conductive paste including a conductive metal on thedielectric layers 111 while allowing them to have a predeterminedthickness.

In addition, the first and second internal electrodes 121 and 122 may bealternately exposed to both end surfaces of the ceramic body in thedirection in which the dielectric layers 111 are stacked, and may beelectrically insulated from each other by the dielectric layer 111disposed therebetween.

That is, the first and second internal electrodes 121 and 122 may beelectrically connected to the first and second external electrodes 131and 132 through portions thereof alternately exposed to the both endsurfaces of the ceramic body 110, respectively.

Therefore, when voltage is applied to the first and second externalelectrodes 131 and 132, electric charges are accumulated between thefirst and second internal electrodes 121 and 122 facing each other. Inthis case, the capacitance of the multilayered ceramic capacitor 100 maybe in proportion to an area of a region overlapped between the first andsecond internal electrodes 121 and 122.

The thickness of the first and second internal electrodes 121 and 122 asdescribed above may be determined according to the use thereof. Forexample, the thickness thereof may be determined to be in a range of 0.2to 1.0 μm in consideration of a size of the ceramic body 110, but thepresent invention is not limited thereto.

Further, the conductive metal included in the conductive paste formingthe first and second internal electrodes 121 and 122 may be nickel (Ni),copper (Cu), palladium (Pd), or an alloy thereof, but the presentinvention is not limited thereto.

In addition, as a method of printing the conductive paste, a screenprinting method, a gravure printing method, or the like, may be used,but the present invention is not limited thereto.

Meanwhile, the first and second external electrodes 131 and 132 may beformed of a conductive paste including a conductive metal, and theconductive metal may be nickel (Ni), copper (Cu), palladium (Pd), gold(Au), or an alloy thereof, but the present invention is not limitedthereto.

According to the embodiment of the present invention, in themultilayered ceramic capacitor 100, a ratio of an area Y of the regionoverlapped between the first and second internal electrodes to a totalarea X of the active layer 115 and the upper cover layer 112 on thecross section of the ceramic body 110 in the length-thickness (L-T)direction may be in a range of 0.5 to 0.9.

Generally, in the case of a product in which the thickness of the lowercover layer of the multilayered ceramic capacitor has been increased inorder to reduce acoustic noise, a crack defect or a delamination defecthas occurred in a sintering process due to a difference in densitybetween a region in which the internal electrodes are formed and aregion in which the internal electrodes are not formed.

However, according to the embodiment of the present invention, in themultilayered ceramic capacitor 100, the ratio of the area Y of theregion overlapped between the first and second internal electrodes tothe total area X of the active layer 115 and the upper cover layer 112on the cross section of the ceramic body 110 in the length-thickness(L-T) direction may be adjusted to be in a range of 0.5 to 0.9, suchthat a multilayered ceramic capacitor having excellent reliability maybe implemented.

Referring to FIG. 2, the total area X of the active layer 115 and theupper cover layer 112 may refer to the total area of a regioncorresponding to X on the cross section of the ceramic body 110 in thelength-thickness (L-T) direction.

The total area X of the active layer and the upper cover layer 112 maybe measured from an image obtained by scanning the cross section of theceramic body 110 in the length direction using the scanning electronmicroscope (SEM) as shown in FIG. 2.

For example, the total area X may be obtained by measuring the totalarea of the region corresponding to X from the image obtained byscanning the cross section of the ceramic body 110 in thelength-thickness (L-T) direction taken along a center of the ceramicbody 110 in the width (W) direction thereof using the scanning electronmicroscope (SEM) as shown in FIG. 2.

Next, referring to FIG. 2, the area Y of the region overlapped betweenthe first and second internal electrodes may refer to an area of aregion corresponding to Y on the cross section of the ceramic body 110in the length-thickness (L-T) direction.

The area Y of the region overlapped between the first and secondinternal electrodes may be measured from the image obtained by scanningthe cross section of the ceramic body 110 in the length direction usingthe scanning electron microscope (SEM) as shown in FIG. 2.

For example, the area Y may be obtained by measuring the area of theregion corresponding to Y from the image obtained by scanning the crosssection of the ceramic body 110 in the length-thickness (L-T) directiontaken along the center of the ceramic body 110 in the width (W)direction using the scanning electron microscope (SEM) as shown in FIG.2.

When the ratio of the area Y of the region overlapped between the firstand second internal electrodes to the total area X of the active layer115 and the upper cover layer 112 on the cross section of the ceramicbody 110 in the length-thickness (L-T) direction is less than 0.5, thedifference in density between the region in which the internalelectrodes are formed and the region in which the internal electrodesare not formed is large, such that the crack or delamination defect maybe generated.

Meanwhile, when the ratio of the area Y of the region overlapped betweenthe first and second internal electrodes to the total area X of theactive layer 115 and the upper cover layer 112 on the cross section ofthe ceramic body 110 in the length-thickness (L-T) direction is greaterthan 0.9, a problem with regard to resistance to moisture may begenerated.

Hereinafter, a relationship between dimensions of components included inthe multilayered ceramic capacitor according to the embodiment of thepresent invention and the acoustic noise will be described.

Referring to FIG. 3, half of a total thickness of the ceramic body 110is defined as A, a thickness of the lower cover layer 113 is defined asB, half of a total thickness of the active layer 115 is defined as C,and a thickness of the upper cover layer 112 is defined as D.

Here, the total thickness of the ceramic body 110 refers to a distancefrom the upper surface S_(T) of the ceramic body 110 to the lowersurface S_(B) thereof, and the total thickness of the active layer 115refers to a distance from an upper surface of a first internal electrode121 formed on the uppermost portion of the active layer 115 to a lowersurface of a second internal electrode 122 formed on the lowermostportion of the active layer 115.

In addition, the thickness B of the lower cover layer 113 refers to adistance from the lower surface of the second internal electrode 122formed on the lowermost portion of the active layer 115 in the thicknessdirection to the lower surface S_(B) of the ceramic body 110, and thethickness D of the upper cover layer 112 refers to a distance from theupper surface of the first internal electrode 121 formed on theuppermost portion of the active layer 115 in the thickness direction tothe upper surface S_(T) of the ceramic body 110.

When voltages having different polarities are applied to the first andsecond external electrodes 131 and 132 formed on both end portions ofthe multilayered ceramic capacitor 100, the ceramic body 110 may beexpanded and contracted in the thickness direction by an inversepiezoelectric effect of the dielectric layer 111, and both end portionsof the first and second external electrodes 131 and 132 may be expandedand contracted as opposed to the expansion and contraction of theceramic body 110 in the thickness direction by a poisson effect.

Here, a center of the active layer 115 is maximally expanded andcontracted from both end portions of the first and second externalelectrodes 131 and 132 in the length direction thereof, which may be acause of the acoustic noise generation.

That is, according to the embodiment of the present invention, in orderto reduce the acoustic noise, points of inflection (PI) formed in bothend surfaces of the ceramic body 110 may be formed in positions lowerthan a center CL_(c) of the ceramic body 110 in the thickness direction,due to a difference between strain generated in a center CL_(A) of theactive layer 115 and strain generated in the lower cover layer 113 atthe time of applying voltage.

In this case, in order to further reduce the acoustic noise, a ratio ofdeviation between the center CL_(A) of the active layer 115 and thecenter CLc of the ceramic body 110, that is, (B+C)/A may be in a rangeof 1.063 to 1.745 (1.063≦(B+C)/A≦1.745).

Further, a ratio of the thickness D of the upper cover layer 112 to thethickness B of the lower cover layer 113, that is, D/B may be in a rangeof 0.021 to 0.422 (0.021≦D/B≦0.422).

In addition, a ratio of the thickness B of the lower cover layer 113 tothe half A of the total thickness of the ceramic body, that is, B/A maybe in a range of 0.329 to 1.522 (0.329≦B/A≦1.522).

Further, a ratio of the half C of the total thickness of the activelayer 115 to the thickness B of the lower cover layer, that is, C/B maybe in a range of 0.146 to 2.458 (0.146≦C/B≦2.458).

Experimental Example

Multilayered ceramic capacitors according to Inventive Examples andComparative Examples were manufactured as follows.

Slurry containing a powder such as barium titanate (BaTiO₃), or thelike, was applied and dried onto a carrier film to prepare a pluralityof ceramic green sheets having a thickness of 1.8 μm.

Next, a conductive paste for nickel internal electrodes was applied tothe ceramic green sheets using a screen to form internal electrodes.

About 370 ceramic green sheets were stacked. In this case, the ceramicgreen sheets on which the internal electrodes were not formed were moredensely stacked below the ceramic green sheets on which the internalelectrodes were formed as compared with above the ceramic green sheetson which the internal electrodes were formed. Isostatic pressing wasperformed on this stacked body at 85° C. and a pressure of 1000 kgf/cm².

The pressed ceramic stacked body was cut into individual chips and thecut chips were de-bound at 230° C. for 60 hours under an air atmosphere.

Then, they were sintered at 1200° C. under reducing atmosphere havingoxygen partial pressure of 10⁻¹¹ atm to 10⁻¹⁰ atm lower than oxygenpartial pressure in a state in which Ni/NiO are balanced, so that theinternal electrodes were not oxidized. A chip size of the multilayeredchip capacitor after sintering was about 1.64 mm×0.88 mm (Length×Width(L×W), 1608 size). In this case, a manufacturing tolerance was in arange of ±0.1 mm, and experiments were performed on samples satisfyingthis range, such that acoustic noise was measured in each sample.

Next, processes such as a process of forming external electrodes, aplating process, and the like, were performed to manufacture themultilayered ceramic capacitor.

TABLE 1 Implemen- A B C D (B + C)/ AN tation of Sample (μm) (μm) (μm)(μm) A B/A D/B C/B (dB) Capacitance  1* 405.5 40.2 365.4 39.9 1.0000.099 0.993 9.090 29.5 OK  2* 436.0 70.4 365.9 69.7 1.001 0.161 0.9905.197 25.7 OK  3* 455.5 90.8 364.3 91.5 0.999 0.199 1.008 4.012 23.1 OK 4* 508.1 24.9 361.1 269.1 0.760 0.049 10.807 14.502 31.2 OK  5* 456.625.2 360.1 167.8 0.844 0.055 6.659 14.290 32.5 OK  6* 527.3 30.2 191.0642.4 0.419 0.057 21.272 6.325 30.3 OK  7* 414.5 30.9 188.8 420.4 0.5300.075 13.605 6.110 30.5 OK  8* 516.2 39.4 360.7 271.5 0.775 0.076 6.8919.155 28.2 OK  9* 446.0 39.8 365.5 121.2 0.909 0.089 3.045 9.183 29.1 OK10* 469.1 40.6 364.2 169.1 0.863 0.087 4.165 8.970 27.9 OK 11* 416.240.7 360.7 70.3 0.964 0.098 1.727 8.862 28.4 OK 12* 428.3 40.8 360.095.7 0.936 0.095 2.346 8.824 28.9 OK 13* 495.9 40.9 364.9 221.0 0.8180.082 5.403 8.922 28.1 OK 14* 435.9 25.0 421.3 4.2 1.024 0.057 0.16816.852 31.6 OK 15* 420.7 70.4 365.9 39.1 1.037 0.167 0.555 5.197 25.7 OK16 431.7 94.8 364.3 40.0 1.063 0.220 0.422 3.843 19.9 OK 17 443.0 103.8389.1 4.0 1.113 0.234 0.039 3.749 19.3 OK 18 443.7 119.8 363.2 41.11.089 0.270 0.343 3.032 18.7 OK 19 447.1 147.3 362.1 22.7 1.139 0.3290.154 2.458 17.9 OK 20 452.8 164.7 360.2 20.4 1.159 0.364 0.124 2.18717.3 OK 21 448.7 170.3 361.0 5.1 1.184 0.380 0.030 2.120 17.2 OK 22470.7 170.4 365.4 40.2 1.138 0.362 0.236 2.144 17.4 OK 23 491.9 220.3360.8 41.8 1.181 0.448 0.190 1.638 16.9 OK 24 500.6 270.2 360.5 9.91.260 0.540 0.037 1.334 16.8 OK 25 516.9 270.4 361.8 39.7 1.223 0.5230.147 1.338 16.7 OK 26 502.1 364.9 312.3 14.7 1.349 0.727 0.040 0.85616.6 OK 27 407.5 421.8 189.1 14.9 1.499 1.035 0.035 0.448 16.6 OK 28445.8 493.3 179.3 39.7 1.509 1.107 0.080 0.363 16.5 OK 29 483.7 632.0160.1 15.2 1.638 1.307 0.024 0.253 16.4 OK 30 520.0 643.4 190.7 15.21.604 1.237 0.024 0.296 16.4 OK 31 486.4 685.3 121.1 45.3 1.658 1.4090.066 0.177 16.4 OK 32 507.2 742.7 120.8 30.1 1.702 1.464 0.041 0.16316.4 OK 33 515.2 773.9 118.2 20.1 1.732 1.502 0.026 0.153 16.4 OK 34524.5 798.2 116.9 16.9 1.745 1.522 0.021 0.146 16.3 OK 35* 533.4 832.4109.8 14.8 1.766 1.561 0.018 0.132 16.3 NG 36* 533.3 841.1 105.3 14.91.775 1.577 0.018 0.125 16.3 NG 37* 534.1 849.7 101.2 16.1 1.780 1.5910.019 0.119 16.3 NG *Comparative Example, AN: acoustic noise

Data of Table 1 were obtained by measuring each dimension from an imageobtained by scanning the cross section of the ceramic body 110 of themultilayered ceramic capacitor 100 in the length-thickness (L-T)direction taken along a center of the ceramic body 100 in the width (W)direction using a scanning electron microscope (SEM) as shown in FIG. 3.

Here, half of a total thickness of the ceramic body 110 was defined asA, a thickness of the lower cover layer 113 was defined as B, half of atotal thickness of the active layer 115 was defined as C, and athickness of the upper cover layer 112 was defined as D, as describedabove.

In order to measure the acoustic noise, after one sample (multilayeredchip capacitor) per a board for measuring acoustic noise was mounted ona printed circuit board in a vertical direction, the board was mountedon a measurement jig.

In addition, DC voltage and voltage variation were applied to bothterminals of the sample mounted on the measurement jig using a DC powersupply and a function generator. The acoustic noise was measured througha mike installed directly above the printed circuit board.

In Table 1, samples 1 to 3 were Comparative Examples of a capacitorhaving a cover symmetry structure in which the thickness B of the lowercover layer 113 and the thickness D of the upper cover layer 112 werealmost the same as each other, and samples 4 to 13 were ComparativeExamples of a capacitor having a structure in which the thickness D ofthe upper cover layer 112 was thicker than the thickness B of the lowercover layer.

Further, samples 14 and 15, and 35 to 37 were Comparative Examples of acapacitor having a structure in which the thickness B of the lower coverlayer 113 was thicker than the thickness D of the upper cover layer 112,and samples 16 to 34 were Inventive Examples of the capacitor accordingto the embodiment of the present invention.

Here, in the case in which (B+C)/A was almost 1, it means that thecenter of the active layer 115 did not largely deviate from the centerof the ceramic body 110. In samples 1 to 3 having the cover symmetrystructure in which the thickness B of the lower cover layer 113 and thethickness D of the upper cover layer 112 were almost the same as eachother, (B+C)/A was almost 1.

When (B+C)/A was larger than 1, it means that the center of the activelayer 115 deviated upwardly from the center of the ceramic body 110, andwhen (B+C)/A was smaller than 1, it means that the center of the activelayer 115 deviated downwardly from the center of the ceramic body 110.

Referring to Table 1, it could be appreciated that in samples 16 to 34,in which the ratio of deviation between the center of the active layer115 and the center of the ceramic body 110, that is, (B+C)/A was in arange of 1.063 to 1.745 (1.063≦(B+C)/A≦1.745), the acoustic noise wassignificantly reduced to be less than 20 dB.

In addition, samples 1 to 15 in which the ratio of deviation between thecenter of the active layer 115 and the center of the ceramic body 110,that is, (B+C)/A was less than 1.063, had a structure in which thecenter of the active layer 115 almost did not deviate from the center ofthe ceramic body 110 or the center of the active layer 115 deviateddownwardly from the center of the ceramic body 110.

In samples 1 to 15 in which (B+C)/A was less than 1.063, the acousticnoise was 23.1 to 32.5 dB. Therefore, it could be appreciated that therewas no effect of reducing the acoustic noise in these samples, ascompared to Inventive Examples.

In addition, in samples 35 to 37 in which the ratio of deviation betweenthe center of the active layer 115 and the center of the ceramic body110, that is, (B+C)/A was more than 1.745, a ratio of capacitance todesired capacitance was low, such that a capacitance defect wasgenerated.

In Table 1, in the case in which the implementation of capacitance (thatis, the ratio of capacitance to desired capacitance) was indicated as“NG,” it means that the ratio of capacitance to desired capacitance wasless than 80%.

Further, it could be appreciated that in Examples in which the ratio(D/B) of the thickness D of the upper cover layer 112 to the thickness Bof the lower cover layer 113 was in a range of 0.021 to 0.422(0.021≦D/B≦0.422), the acoustic noise was significantly reduced.

On the other hand, it could be appreciated that in Comparative Examplesin which the ratio (D/B) of the thickness D of the upper cover layer 112to the thickness B of the lower cover layer 113 was more than 0.422, theacoustic noise was not reduced.

In the case in which the ratio (D/B) of the thickness D of the uppercover layer 112 to the thickness B of the lower cover layer 113 was lessthan 0.021, the thickness B of the lower cover layer 113 was excessivelythick as compared to the thickness D of the upper cover layer 112, suchthat cracks or delamination may be generated. In addition, due to theexcessively low capacitance as compared to the desired capacitance, thecapacitance defect may be generated.

It could be appreciated that the acoustic noise was further reduced tobe less than 18 dB in samples 19 to 34, in which the ratio (B/A) of thethickness B of the lower cover layer 113 to the thickness A of theceramic body 110 and the ratio (C/B) of the thickness C of the activelayer 115 to the thickness B of the lower cover layer 113 were in arange of 0.329 to 1.522 and in a range of 0.146 to 2.458, respectively(0.329≦B/A≦1.522 and 0.146≦C/B≦2.458).

On the other hand, in samples 35 to 37 in which the ratio (B/A) of thethickness B of the lower cover layer 113 to the thickness A of theceramic body 110 was more than 1.522, or the ratio (C/B) of thethickness C of the active layer 115 to the thickness B of the lowercover layer 113 was less than 0.146, the capacitance thereof wasexcessively low as compared to the desired capacitance, such that thecapacitance defect may be generated.

The following Table 2 shows experimental results obtained by performinga reliability test on multilayered ceramic capacitor samples accordingto the ratio of the area Y of the region overlapped between the firstand second internal electrodes to the total area X of the active layer115 and the upper cover layer 112 on the cross section of the ceramicbody 110 in the length-thickness (L-T) direction.

The reliability test was measured by a 8585 test and a soldering heatresistance test as shown in Table 2.

The 8585 test was performed by measuring the reliability of themultilayered ceramic capacitor samples at a temperature of 85° C. and ahumidity of 85%, and the number of samples having defects among 200samples was indicated as a numerical value.

The soldering heat resistance test was performed by measuring a changein capacitance of the multilayered ceramic capacitor samples after themultilayered ceramic capacitor samples were soaked in a solder bathfilled with a molten solder at 270° C. for 10 seconds, and the number ofsamples determined as the defective samples due to the significantchange in capacitance among 200 samples was indicated as a numericalvalue.

TABLE 2 8585 Test Soldering Heat (Temperature: 85° C., Resistance TestY/X Humidity: 85%) (270° C., 10 seconds) *1 0.4 0/200 37/200  *2 0.450/200 18/200  3 0.5 0/200 0/200 4 0.6 0/200 0/200 5 0.7 0/200 0/200 60.8 0/200 0/200 7 0.9 0/200 0/200 *8 0.95 24/200  0/200 *ComparativeExample

Referring to Table 2, it could be appreciated that in samples 1, 2, and8, which were out of the numerical range of the present invention, thedefects were generated therein in the reliability test, such that thereliability of the capacitors was problematic.

Meanwhile, it could be appreciated that in samples 3 to 7, which were inthe numerical range of the present invention, the ratio of the area Y ofthe region overlapped between the first and second internal electrodesto the total area X of the active layer 115 and the upper cover layer112 was in the range of 0.5 to 0.9, and the reliability of thecapacitors was excellent.

Board for Mounting Multilayered Ceramic Capacitor

Referring to FIGS. 4 and 5, a board 200 for mounting a multilayeredceramic capacitor 100 according to the embodiment of the presentinvention may include a printed circuit board 210 on which themultilayered ceramic capacitor 100 is horizontally mounted and first andsecond electrode pads 221 and 222 formed on the printed circuit board210 to be spaced apart from each other.

In this case, the multilayered ceramic capacitor 100 may be electricallyconnected to the printed circuit board 210 by soldering 230 in a statein which a lower cover layer 113 is disposed to be a lower portion ofthe capacitor and first and second external electrodes 131 and 132 arepositioned on the first and second electrode pads 221 and 222 so as tocontact the first and second electrode pads 221 and 222, respectively.

When voltage is applied in a state in which the multilayered ceramiccapacitor 100 is mounted on the printed circuit board 210 as describedabove, acoustic noise may be generated.

Here, sizes of the first and second electrode pads 221 and 222 maybecome an indicator for determining an amount of the solder 230connecting the first and second external electrodes 131 and 132 of themultilayered ceramic capacitor 100 to the first and second electrodepads 221 and 222, and a level of the acoustic noise may be adjustedaccording to the amount of the solder 230.

Referring to FIG. 6, when voltages having different polarities areapplied to the first and second external electrodes 131 and 132 formedon both end portions of the multilayered ceramic capacitor 100 in astate in which the multilayered ceramic capacitor 100 is mounted on theprinted circuit board 210, the ceramic body 110 may be expanded andcontracted in the thickness direction by the inverse piezoelectriceffect of the dielectric layer 111, and both end portions of the firstand second external electrodes 131 and 132 may be expanded andcontracted as opposed to expansion and contraction of the ceramic body110 in the thickness direction by the poisson effect.

Here, a center of the active layer 115 is significantly expanded andcontracted at both end portions of the first and second externalelectrodes 131 and 132 in the length direction, which may be a cause ofthe acoustic noise generation.

When both end surfaces of the multilayered ceramic capacitor 100 in thelength direction are maximally expanded, outward expansive force isgenerated in an upper portion of the solder 230 by expansion, and forceis generated in a lower portion of the solder 230 to act on the externalelectrodes due to the outward expansive force created by the expansion.

Therefore, in the case in which points of inflection (PI) formed in bothend surfaces of the ceramic body 110 due to a difference between straingenerated in the center CL_(A) of the active layer 115 and straingenerated in the lower cover layer 113 are formed in positions lowerthan a height of the solder 230 as in the present embodiment, theacoustic noise may be further reduced.

As set forth above, according to embodiments of the present invention,acoustic noise may be reduced at the time of mounting a multilayeredcapacitor on a printed circuit board by reducing vibrations generated inthe multilayered ceramic capacitor.

In addition, according to embodiments of the present invention, amultilayered ceramic capacitor having excellent reliability may beimplemented by reducing a change in density between a region in whichthe internal electrodes re formed and a region in which the internalelectrodes are not formed.

While the present invention has been shown and described in connectionwith the embodiments, it will be apparent to those skilled in the artthat modifications and variations can be made without departing from thespirit and scope of the invention as defined by the appended claims.

What is claimed is:
 1. A multilayered ceramic capacitor comprising: aceramic body in which a plurality of dielectric layers are stacked; anactive layer including a plurality of first and second internalelectrodes formed to be alternately exposed to both end surfaces of theceramic body, having the dielectric layer interposed therebetween, toform capacitance; an upper cover layer formed above the active layer alower cover layer formed below the active layer and being thicker thanthe upper cover layer; and first and second external electrodes formedto cover the both end surfaces of the ceramic body, wherein a ratio ofan area Y of a region overlapped between the first and second internalelectrodes to a total area X of the active layer and the upper coverlayer on a cross section of the ceramic body in length-thickness (L-T)directions is in a range of 0.5 to 0.9.
 2. The multilayered ceramiccapacitor of claim 1, wherein when half of a total thickness of theceramic body is defined as A, a thickness of the lower cover layer isdefined as B, half of a total thickness of the active layer is definedas C, and a thickness of the upper cover layer is defined as D, a ratio((B+C)/A) of deviation between a center of the active layer and a centerof the ceramic body is in a range of 1.063 to 1.745(1.063≦(B+C)/A≦1.745).
 3. The multilayered ceramic capacitor of claim 1,wherein when a thickness of the lower cover layer is defined as B and athickness of the upper cover layer is defined as D, a ratio (D/B) of thethickness D of the upper cover layer to the thickness B of the lowercover layer is in a range of 0.021 to 0.422 (0.021≦D/B≦0.422).
 4. Themultilayered ceramic capacitor of claim 1, wherein when half of a totalthickness of the ceramic body is defined as A and a thickness of thelower cover layer is defined as B, a ratio (B/A) of the thickness B ofthe lower cover layer to the half A of the total thickness of theceramic body is in a range of 0.329 to 1.522 (0.329≦B/A≦1.522).
 5. Themultilayered ceramic capacitor of claim 1, wherein when a thickness ofthe lower cover layer is defined as B and half of a total thickness ofthe active layer is defined as C, a ratio (C/B) of the half C of thetotal thickness of the active layer to the thickness B of the lowercover layer is in a range of 0.146 to 2.458 (0.146≦C/B≦2.458).
 6. Themultilayered ceramic capacitor of claim 1, wherein points of inflection(PI) formed in the both end surfaces of the ceramic body are formed inpositions lower than a center of the ceramic body in a thicknessdirection due to a difference between strain generated in a center ofthe active layer and strain generated in the lower cover layer whenvoltage is applied thereto.
 7. A board for mounting a multilayeredceramic capacitor, the board comprising: a printed circuit board havingfirst and second electrode pads formed thereon; and a multilayeredceramic capacitor mounted on the printed circuit board, wherein themultilayered ceramic capacitor includes: a ceramic body in which aplurality of dielectric layers are stacked; an active layer including aplurality of first and second internal electrodes formed to bealternately exposed to both end surfaces of the ceramic body, having thedielectric layer interposed therebetween, to form capacitance; an uppercover layer formed above the active layer; a lower cover layer formedbelow the active layer and being thicker than the upper cover layer; andfirst and second external electrodes formed on the both end surfaces ofthe ceramic body and connected to the first and second electrode pads bysoldering, and a ratio of an area Y of a region overlapped between thefirst and second internal electrodes to a total area X of the activelayer and the upper cover layer on a cross section of the ceramic bodyin length-thickness (L-T) directions is in a range of 0.5 to 0.9.
 8. Theboard of claim 7, wherein when half of a total thickness of the ceramicbody is defined as A, a thickness of the lower cover layer is defined asB, half of a total thickness of the active layer is defined as C, and athickness of the upper cover layer is defined as D, a ratio ((B+C)/A) ofdeviation between a center of the active layer and a center of theceramic body is in a range of 1.063 to 1.745 (1.063≦(B+C)/A≦1.745). 9.The board of claim 7, wherein when a thickness of the lower cover layeris defined as B and a thickness of the upper cover layer is defined asD, a ratio (D/B) of the thickness D of the upper cover layer to thethickness B of the lower cover layer is in a range of 0.021 to 0.422(0.021≦D/B≦0.422).
 10. The board of claim 7, wherein half of a totalthickness of the ceramic body is defined as A and a thickness of thelower cover layer is defined as B, a ratio (B/A) of the thickness B ofthe lower cover layer to the half A of the total thickness of theceramic body is in a range of 0.329 to 1.522 (0.329≦B/A≦1.522).
 11. Theboard of claim 7, wherein when a thickness of the lower cover layer isdefined as B and half of a total thickness of the active layer isdefined as C, a ratio (C/B) of the half C of the total thickness of theactive layer to the thickness B of the lower cover layer is in a rangeof 0.146 to 2.458 (0.146≦C/B≦2.458).
 12. The board of claim 7, whereinpoints of inflection (PI) formed in the both end surfaces of the ceramicbody are formed in positions lower than a height of the soldering due toa difference between strain generated in a center of the active layerand strain generated in the lower cover layer when voltage is appliedthereto.